  • Wind turbine blade putty
  • Wind turbine blade putty
Wind turbine blade puttyWind turbine blade putty

Wind turbine blade putty

  • Product Item : 725-S07-14
  • Category: Industrial Coatings
  • A three-component solvent-free polyurethane putty. Excellent flexibility and adhesion, fast drying, easy to polish.
  • TDS INQUIRY   EMAIL

Produce Description

A three-component solvent-free polyurethane putty.

Excellent flexibility and adhesion, fast drying, easy to polish.

Intended Uses

Designed  for  wind  turbine  blade. As a putty for repairing  the  surface defects on epoxy or polyester based FRP wind turbine blade.

Product Information

Volume Solids

≥98%

Finish/Sheen

No applicable

Film Thickness

Consultation

Mix ratio

Part A : Part B = 3.2:1~3.3:1Volume5.5:1~5.7:1 mass),Part C: 0.4-0.6% by total weight.

Thinner

Not    recommended.    Use 725-NX-701    thinner     only    in exceptional circumstances (mass 5%)

Cleaner

725-NX-701

Induction Period

Not necessary

Flash Point

Part A

Not available

Part B

Higher than 100

Part C

Higher than 31

Mixed paint

Not available

Method of Application

Knife

Drying Information

5

15

25

35

Touch Dry

110min

85min

30min

20min

Hard Dry

4h

3h

1h

0.6h

Pot Life with Part C

5min

4min

3min

2min

Pot Life without Part C

25h

24h

10h

8h

Overcoating Data

Substrate Temperature

Overcoated by

5

15

25

35

Min        Max

Min        Max

Min Max

Min Max

725-S06-15

4h 20d

3h 14d

2h         10d

1.5h 7d

Pack Size

Part A

10kg/5L in 10L container

Part B

1.8kg/1.5L in 2L container

Part C

0.4kg/0.4L in 0.5L container

Storage

Store in well ventilated and dry conditions when temperature is -10℃~40℃and RH is less than 90%. Keep  away from  hot and fire.Shelf Life: 12months minimum at 25℃Subject  to re-inspection thereafter.

Systems and Compatibility
Consult your Representative for the systems best suited for the surfaces to be protected.
Surface Preparation
Clean dust,grease,water droplets and other pollutants.Using pneumatic grinding  tools  or manual with 120 sandpaper to clean up blade surface thoroughly. Grinding is required before any recoating.
Curing condition
The suitable temperature for applying 725-S07-14 is 5~35℃.
According to the ratio of mass ratio A: B = 5.6:1, pour the B component into the A component, stir well and stand aside for use. Take out appropriate amount of A-B mixed putty, add in the total weight of the mixed putty about 0.4%~0.6% of the Part C, stir evenly and immediately scrape.


CONTACT US

Name: Lily Lu

Mobile:86-13922763266

Tel:86-20-38993165

Whatsapp:86-13922763266

Email:lilylu@huisins.com

Add:Room 206, Building 21, LongTeng Xing Cheng, No.68 LongTeng South Road, DongXiao Town, XinLuo District, LongYan City, FuJian Province. China