Aluminium Heat-Resisiting Paint-Silver

Aluminium Heat-Resisiting Paint-Silver

Product Description:

- Model:725-W61-01

- One pack, dry at room or higher temperature

- On surface likely to reach up to 300~350℃

- VOC less than 535g/L

Intended Uses:

- For use at Newbuilding, Maintenance and Repair.

- For use at all kinds of high temperature equipment,such as ship stacks.

Product Information:

Volume Solids:40%±2%                  Finish/Sheen:  Gloss

Film Thickness(μm)

Min

Typical

Max

Dryfilm Thickness

20

30

40

Wetfilm Thickness

50

75

100

Theoretical Coverage(m2/L)

20

13.3

10

Mix Ratio:one pack

Method of Application

 

Airless Spray

Recommended

Tip size range:0.38-0.53mm

Output pressure:17MPa

Air Spray

Tip size range:2.0-3.0mm

Output pressure:0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%).

Cleaner

JX-061

Induction Period

Not necessary

 Drying Information:

 

10℃

25℃

35℃

Touch Dry

1h

30min

20min

Hard Dry

8h

6h

3h

Overcoating Data:

 

10℃

25℃

35℃

Overcoated by

Min Max

Min Max

Min Max

725-W61-01

8h

6h

3h

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ℃,Subject to re-inspection thereafter.

Pack Size: 19.8kg/18L in 20 L container

Flash Point: Greater than 28℃

Systems and Compatibility:

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation:

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Newbuilding:

Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5GB/T 8923.1-2011.The weld seams areas could be cleaned to St3GB/T 8923.1-2011using power tool.

Apply 725-W61-01 before oxidation occurs. If oxidation has occurred, the entire oxidized area should be reblasted to the standard specified above.

Repair/On Board Maintenance:

The areas to be repaired should be cleaned to P St3 GB/T 8923.2-2008 by mechanical method or higher level of surface prepared to P Sa2.5 GB/T 8923.2-2008by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

Limitations:

1) Apply in good weather. Temperature of the surface to be coated must be least 3 ℃above the dew point when the humidity is lower than 85%.

2) The dry time and overcoating interval may change according to the environment factors.

3) Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement:

  • The data in the sheet base on the information from the laboratory and practice.
  • The application may exceed the control, so we only ensure our product quality.
  • We own the right of the data sheet modification without informing.