Alkyd Primer-Iron Red/Silver Red

Alkyd Primer-Iron Red/Silver Red

Product Description:

- Model: 725-C53-1

-A quick drying, single pack alkyd primer

-Overcoated time is not limited

-VOC less than 390g/L

Intended Uses

-For use in all above water areas.

-For use at Newbuilding, Maintenance and Repair or On Board Maintenance.

Product Information

Volume Solids:55%±2%                  Finish/Sheen:  Matt

Film Thickness(μm)

Min

Typical

Max

Dryfilm Thickness

50

80

150

Wetfilm Thickness

91

145

273

Theoretical Coverage(m2/L)

11

6.9

3.7

Mix Ratio: Single pack

Method of Application

 

Airless Spray

Recommended

Tip size range:0.38-0.53mm

Output pressure:17MPa

Air Spray

Tip size range:2.0-3.0mm

Output pressure:0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%).

Cleaner

CX-101

Induction Period

Not applicable

Drying Information 

 

-5℃

5℃

25℃

35℃

Touch Dry

2h

1h

 30min

20min

Hard Dry

48h

48h

24h

16h

Pot Life

Not applicable

Overcoating Data

   -5℃

        5℃

25℃   

        35℃   

Min Max

Min Max  

   Min Max

   Min Max

48h

       24h

20h      

      16h

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ℃,Subject to re-inspection thereafter.

Pack Size: 26.5kg/18L in 20 L container.

Flash Point: Greater than 28℃.

Systems and Compatibility: 

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

 Surface Preparation:

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Newbuilding 

Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5GB/T 8923.1-2011.The weld seams areas could be cleaned to St3GB/T 8923.1-2011using power tool.

The areas to be repaired should be cleaned to P St3  GB/T 8923.2-2008  by mechanical method or higher level of surface prepared to P Sa2.5  GB/T8923.2-2008by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

Limitations:

Apply 725-C53-1 before oxidation occurs. If oxidation has occurred, the entire oxidized area should be reblasted to the standard specified above.

Duty statement:

The data in the sheet base on the information from the laboratory and practice.

The application may exceed the control, so we only ensure our product quality.

We own the right of the data sheet modification without informing.