Anodic Shield Coating-Yellow

Anodic Shield Coating-Yellow

Product Description:

- Model:725-8702-5

- A two pack epoxy coating

- Quickly drying and applying

- VOC is 0g/L

Intended Uses

- Shielding coating for marine applied current cathodic protection system and protective coating for pipe joint.

- For hull and steel structure to fill holes caused by cavitation corrosion or pitting.

Product Informatio:

Volume Solids:100%

Film Thickness(μm)

Min

Typical

Max

Dryfilm Thickness

500

1000

2000

Wetfilm Thickness

500

1000

2000

Theoretical Coverage(m2/L)

2

1

0.5

Mix Ratio:1:1(mass)

Method of Application

 

Airless Spray

Not Recommended

Air Spray

Not Recommended

Brush/Roller

Not Recommended

Scraping

Recommended

Thinner

Not recommended

Cleaner

HX-501

Induction Period 

          5℃

        15℃

25℃

35℃

   15min

   10min

5min

2min

Drying Information 

 

5℃

15℃

25℃

35℃

Touch Dry

8h

6h

4h

3h

Hard Dry

36h

24h

20h

16h

Pot Life

2h

1.5h

1h

20min

Overcoating Data

        5℃       

        15℃ 

25℃      

        35℃         

    Min Max

Min Max

    Min Max

     Min Max

   24h 14d

     20h 10d

16h 7d

     12h5d

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ℃,Subject to re-inspection thereafter.

Pack Size:

Part A: 4kg/3L in4L container 

Part B: 4kg/3L in 4L container

Flash Point: Not

Systems and Compatibility: 

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation: 

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Limitations:

This product will not cure adequately below 5℃ ,For maximum performance ambient curing temperature should be above 10℃.

Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.

If part A thickened or dried, it should be heated to about 80 ℃by oven until the viscosity recovered. It can be used again when the temperature dropped.

If part B thickened when the environment temperature was too low, it should be heated to about 80 ℃ by oven until the viscosity recovered. No heating for too long time. It can be used again when the temperature dropped.

The dry time and overcoating interval may change according to the environment factors.

Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement:

The data in the sheet base on the information from the laboratory and practice.

The application may exceed the control, so we only ensure our product quality.

We own the right of the data sheet modification without informing.