High Build Epoxy Intermediate Coating-Grey/White

High Build Epoxy Intermediate Coating-Grey/White

Product Description:

- Model: 725-H53-87

- A two pack high build epoxy coating.

- Suitable for application at low temperature.

- VOC less than180g/L

Intended Uses:

- For use in atmospheric environment protection.

- For use at offshore facility, chemical plant, and wind power tower, etc.

Product Information:

Volume Solids:80%±2%                  Finish/Sheen:  Gloss

Typical Film Thickness

200microns dry (250microns wet)

Theoretical Coverage(m2/L)

4m2/L at typical film thickness

Mix Ratio: 2:1(volume)3.4:1(mass)

Method of Application

 

Airless Spray

Recommended

 

Tip size range:0.38-0.53mm

 

Output pressure:≥17MPa

Air Spray

Tip size range:2.0-3.0mm

 

Output pressure:≥0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use HX-501 only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

Not necessary

 Drying Information:

 

-5℃

 10℃

25℃

35℃

Touch Dry

6h

2h

1h

0.5h

Hard Dry

48h

24h

18h

12h

Pot Life

6h

4h

3h

2h

Overcoating Data:

 

Substrate Temperature

 

-5℃

 10℃

25℃

35℃

Overcoated by

Min Max

Min Max

Min Max

Min Max

725-J43-5

48h

24h

18h

12h

725-BS43-91

48h

24h

18h

12h

725-H42-30

48h

36h

20h

12h

Storage:

Store in cool and dry conditions,Well ventilate.Keep away from hot and fire. Shelf Life: 12 months

minimum at 25 ℃,Subject to re-inspection thereafter.

Pack Size:

Part A: 22kg/13.5L in 20L container

Part B: 6.5kg/6.5L in 9.25L container

Flash Point:

Part A: Greater than 31℃

Part B: Greater than 28℃

Mixed pant: Greater than 31℃

Surface Preparation:

All surfaces to be coated should be clean, dry and free from contamination.

Primed Surfaces

The primer surface should be dry free from all contamination and 725-H53-87must be applied within the overcoating intervals specified (consult the relevant product data sheet).

Areas of breakdown, damage etc., should be prepared to the specified standard (e.gSa2½(GB/T 8923.1-2011)or Abrasive Blasting, or Power Tool Cleaning) and patch primed prior to the application of 725-H53-87.

Metallic Zinc Primed Surfaces

Ensure that surface of the primer is clean, dry and free from contamination and zinc salts before application of 725-H53-87. Ensure zinc primers are fully cured before overcoating.

Limitations:

1)For maximum performance ambient curing temperature should be above 5℃.

2)In common with all epoxy base coatings, 725-H53-87 will exhibit chalking of the firm on UV exposure.

3)Apply in good weather. Temperature of the surface to be coated must be least 3℃ above the dew point when the humidity is lower than 85%.

4)The dry time and overcoating interval may change according to the environment factors.

5)Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement:

● The data in the sheet base on the information from the laboratory and practice.

● The application may exceed the control, so we only ensure our product quality.

● We own the right of the data sheet modification without informing.